BASF Ultrason S 3010 PSU 物性表
物理性能额定值 (公制)额定值 (英制)测试方法
密度1.24 g/cc0.0448 lb/in³ISO 1183
吸水率0.80 %0.80 %ISO 62
平衡吸湿0.30 %0.30 %23°C/50% R.H.; ISO 62
粘度测试72 cm³/g72 cm³/gViscosity number
线性成型收缩率,Flow0.0070 cm/cm0.0070 in/inISO 294
线性成型收缩率，横向0.0074 cm/cm0.0074 in/inISO 294
熔体流动速率40 g/10 min
@Load 10.0 kg, Temperature 360 °C
40 g/10 min
@Load 22.0 lb, Temperature 680 °F
ISO 1133
机械性能额定值 (公制)额定值 (英制)测试方法
球压硬度135 MPa19600 psiISO 2039-1
抗张强度(断裂)75.0 MPa10900 psi5mm/min; ISO 527-2
抗张强度20.0 MPa
@Strain 1.00 %, Temperature 160 °C
2900 psi
@Strain 1.00 %, Temperature 320 °F
ISO 527

27.0 MPa
@Strain 1.00 %, Temperature 23.0 °C
3920 psi
@Strain 1.00 %, Temperature 73.4 °F
ISO 527

35.0 MPa
@Strain 2.00 %, Temperature 160 °C
5080 psi
@Strain 2.00 %, Temperature 320 °F
ISO 527

47.0 MPa
@Strain 2.00 %, Temperature 23.0 °C
6820 psi
@Strain 2.00 %, Temperature 73.4 °F
ISO 527

70.0 MPa
@Strain 4.00 %, Temperature 23.0 °C
10200 psi
@Strain 4.00 %, Temperature 73.4 °F
ISO 527
抗张强度(屈服)75.0 MPa10900 psi50mm/min; ISO 527-2

40.0 MPa
@Temperature 140 °C
5800 psi
@Temperature 284 °F


58.0 MPa
@Temperature 100 °C
8410 psi
@Temperature 212 °F


68.0 MPa
@Temperature 60.0 °C
9860 psi
@Temperature 140 °F


75.0 MPa
@Temperature 20.0 °C
10900 psi
@Temperature 68.0 °F

伸长率 (断裂)5.7 %5.7 %5mm/min; ISO 527-2
屈服伸长率5.7 %5.7 %50mm/min; ISO 527-2

0.50 %
@Time 3600 sec, Pressure 10.0 MPa
0.50 %
@Time 1.00 hour, Pressure 1450 psi
ISO 899

0.55 %
@Pressure 10.0 MPa, Time 360000 sec
0.55 %
@Pressure 1450 psi, Time 100 hour
ISO 899

0.56 %
@Pressure 10.0 MPa, Time 3.60e+7 sec
0.56 %
@Pressure 1450 psi, Time 10000 hour
ISO 899

0.80 %
@Time 3600 sec, Pressure 20.0 MPa
0.80 %
@Time 1.00 hour, Pressure 2900 psi
ISO 899

0.90 %
@Pressure 20.0 MPa, Time 360000 sec
0.90 %
@Pressure 2900 psi, Time 100 hour
ISO 899

1.3 %
@Time 3600 sec, Pressure 30.0 MPa
1.3 %
@Time 1.00 hour, Pressure 4350 psi
ISO 899

1.4 %
@Pressure 30.0 MPa, Time 360000 sec
1.4 %
@Pressure 4350 psi, Time 100 hour
ISO 899

1.5 %
@Pressure 30.0 MPa, Time 3.60e+7 sec
1.5 %
@Pressure 4350 psi, Time 10000 hour
ISO 899

1.9 %
@Time 3600 sec, Pressure 40.0 MPa
1.9 %
@Time 1.00 hour, Pressure 5800 psi
ISO 899

2.0 %
@Pressure 20.0 MPa, Time 3.60e+7 sec
2.0 %
@Pressure 2900 psi, Time 10000 hour
ISO 899

2.0 %
@Pressure 40.0 MPa, Time 360000 sec
2.0 %
@Pressure 5800 psi, Time 100 hour
ISO 899

2.0 %
@Time 3600 sec, Pressure 42.0 MPa
2.0 %
@Time 1.00 hour, Pressure 6090 psi
ISO 899

2.2 %
@Pressure 42.0 MPa, Time 360000 sec
2.2 %
@Pressure 6090 psi, Time 100 hour
ISO 899

2.4 %
@Pressure 40.0 MPa, Time 3.60e+7 sec
2.4 %
@Pressure 5800 psi, Time 10000 hour
ISO 899

2.5 %
@Pressure 42.0 MPa, Time 3.60e+7 sec
2.5 %
@Pressure 6090 psi, Time 10000 hour
ISO 899
Creep Strength17.0 MPa
@Time 3.60e+7 sec
2470 psi
@Time 10000 hour
in water at 95°C

20.0 MPa
@Time 3.60e+6 sec
2900 psi
@Time 1000 hour
in water at 95°C

25.0 MPa
@Time 360000 sec
3630 psi
@Time 100 hour
in water at 95°C

32.0 MPa
@Time 36000 sec
4640 psi
@Time 10.0 hour
in water at 95°C
弹性模量2.00 GPa
@Temperature 140 °C
290 ksi
@Temperature 284 °F
ISO 527

2.30 GPa
@Temperature 100 °C
334 ksi
@Temperature 212 °F
ISO 527

2.49 GPa
@Temperature 60.0 °C
361 ksi
@Temperature 140 °F
ISO 527

2.51 GPa
@Temperature 20.0 °C
364 ksi
@Temperature 68.0 °F
ISO 527
拉伸模量2.60 GPa377 ksiISO 527-2
Fatigue Strength25.0 MPa
@# of Cycles 1.00e+7
3630 psi
@# of Cycles 1.00e+7


30.0 MPa
@# of Cycles 1.00e+6
4350 psi
@# of Cycles 1.00e+6


40.0 MPa
@# of Cycles 100000
5800 psi
@# of Cycles 100000


50.0 MPa
@# of Cycles 10000
7250 psi
@# of Cycles 10000

剪切模量0.0250 GPa
@Temperature 200 °C
3.63 ksi
@Temperature 392 °F
ISO 6721

0.800 GPa
@Temperature 175 °C
116 ksi
@Temperature 347 °F
ISO 6721

0.900 GPa
@Temperature 100 °C
131 ksi
@Temperature 212 °F
ISO 6721

0.950 GPa
@Temperature 50.0 °C
138 ksi
@Temperature 122 °F
ISO 6721
悬壁梁缺口冲击强度5.50 kJ/m²2.62 ft-lb/in²ISO 180/A

5.00 kJ/m²
@Temperature 120 °C
2.38 ft-lb/in²
@Temperature 248 °F
ISO 179/1eA

6.00 kJ/m²
@Temperature -30.0 °C
2.86 ft-lb/in²
@Temperature -22.0 °F
ISO 180/A

10.0 kJ/m²
@Temperature 50.0 °C
4.76 ft-lb/in²
@Temperature 122 °F
ISO 179/1eA

13.0 kJ/m²
@Temperature -25.0 °C
6.19 ft-lb/in²
@Temperature -13.0 °F
ISO 179/1eA
简支梁无缺口冲击强度NBNBISO 179/1eU

NB
@Temperature -30.0 °C
NB
@Temperature -22.0 °F
ISO 179/1eU
简支梁缺口冲击强度0.550 J/cm²2.62 ft-lb/in²ISO 179/1eA

0.600 J/cm²
@Temperature -30.0 °C
2.86 ft-lb/in²
@Temperature -22.0 °F
ISO 179/1eA
拉伸蠕变模量(1000 hr)2500 MPa363000 psiISO 899-1
电气性能额定值 (公制)额定值 (英制)测试方法
体积电阻率>= 1.00e+13 ohm-cm>= 1.00e+13 ohm-cmIEC 60093
表面电阻>= 1.00e+14 ohm>= 1.00e+14 ohmIEC 60093
介电常数3.1
@Frequency 100 Hz
3.1
@Frequency 100 Hz
IEC 60250

3.1
@Frequency 1.00e+6 Hz
3.1
@Frequency 1.00e+6 Hz
IEC 60250
介电强度37.0 kV/mm940 kV/inIEC 60243-1
耗散因数0.00080
@Frequency 100 Hz
0.00080
@Frequency 100 Hz
IEC 60250

0.0064
@Frequency 1.00e+6 Hz
0.0064
@Frequency 1.00e+6 Hz
IEC 60250
相比耐漏电起痕指数(CTI)125 V125 VTest Liquid A & B; IEC 60112
热性能额定值 (公制)额定值 (英制)测试方法
线形热膨胀系数 - 流动53.0 µm/m-°C
@Temperature 23.0 - 80.0 °C
29.4 µin/in-°F
@Temperature 73.4 - 176 °F
ISO 11359-1/-2

60.0 µm/m-°C
@Temperature 140 - 180 °C
33.3 µin/in-°F
@Temperature 284 - 356 °F
ISO 11359-1/-2